How To Successfully Weld Aluminum with a Compact MIG Welder

admin

When it comes to welding aluminum items around the home or garage, there are a few misconceptions we hope to clear up: 1) That you need to invest in a $4,000 welding machine and be highly skilled to have success; 2) With no practice you can make excellent welds the first time the wire feed welder is taken out of the box; and 3) You need an expensive spool gun suited for aluminum.The truth is that with practice, the right equipment and proper set-up, a compact MIG welder will be able to tackle occasional aluminum welding jobs. Using your MIG welder, you will be able to work on a variety of items around your home and yard, such as grills, railings, backyard furniture, boat docks and even decorative elements. Compact MIG welders, such as the SP, Weld-Pak or Pro models from Lincoln Electric, are available at distributors and retail outlets.A Word About AluminumEven home welding enthusiasts who have experience welding steel may find a switch to aluminum challenging. Here's why: Because of the softness of aluminum wire, it is more difficult to feed. In addition, wire diameters and machine settings normally used for steel may not be appropriate for aluminum. In order to be successful, ask yourself these questions:What Machine Do I Need?The first decision is what type of machine is right for the job. Keep in mind that a 115 volt wire feeder welder can handle jobs that range from 22 to 12 gauge and with moderate preheating, you can probably weld as thick as 1/8". Be aware that preheating should be limited to 250 degrees F maximum.Another option is a 230 volt machine which can weld from 22 gauge all the way to 3/16". Proper preheat can take the range to 1/4". If you will need to weld a broader range of aluminum thicknesses, consider investing in the 230v machine.Remember, if you plan on doing regular aluminum fabrication, you will need a heavy duty machine. The 115 volt and 230 volt compact MIG welder models are acceptable for occasional aluminum jobs, but not recommended for heavy duty aluminum use. For daily production welding on heavier aluminum, consider a welder that has greater than 200 amps output.After you have chosen your input voltage, another common question you will be asked when selecting a welder is whether you want a continuous or tapped voltage control model.A continuous voltage control model lets you set an infinite range of voltage within the rating of the machine, allowing more adjustability, fine tuning and precise control. This permits you to more easily adapt the voltage to your application and particular skill level.If you're on a budget, opt for the tapped control unit. This machine has a rotary switch with four or five fixed voltage choices. It will not give you the control of a continuous model, but it can be slightly easier to get up to speed with and costs less to purchase and will be adequate for most applications.What Type of Welds Can be Made?For these types of machines, it is best to make welds in the horizontal and flat positions. In general, fillet welds in lap joints are made more easily than groove welds in butt joints. Fillet welds in tee joints are preferred over corner joints. Keep in mind that home welding by an amateur is not recommended for critical welds where failure could result in serious injury.What Type of Shielding Gas is Required?MIG welding aluminum is different than welding steel when it comes to shielding gas requirements. For aluminum, 100 percent argon is the gas of choice, whereas steel welding calls for a mixed gas or 100 percent CO2 gas. The good news is that no special equipment is needed - your existing regulators (with the exception of CO2 regulators) and gas hoses can be used for both pure blends and mixed gases.What Polarity Setting is Needed?All MIG welding, including on aluminum materials, requires electrode positive polarity, while flux-cored processes typically use electrode negative. If you are switching your wire feed welder between processes, make sure to switch your polarity. This is a common mistake that many beginning welders make.What Aluminum Wire Electrode Alloy Type Should I Buy?You will not obtain good results attempting to weld on aluminum with a steel wire electrode.Instead, our recommendation is that compact MIG welders should be limited to .035" diameter 4043 aluminum alloy filler metal. A 5356 aluminum alloy electrode may commonly be recommended by retailers and distributors, since it is a stiffer wire and can be easier to feed. However, with these types of wire feed welders, there is often not enough amperage to achieve a good weld with 5356. Even though 4043 is a softer wire, following the proper steps outlined below will ensure good feedability.Do not use other diameter wires. Specifically, you should avoid 0.030" wire (it is difficult to feed) and 3/64" wire (these compact machines do not typically produce enough current to reliably melt this diameter of wire).How Do I Set-Up My Machine to Weld Aluminum?Now that you know the type of machine you want and its capabilities/limitations, it is important to know how best to set it up. Follow these tips:Purchase an Aluminum Feeding KitAttention to feeding issues is much more critical when it comes to aluminum welding. It is highly recommended that you purchase an aluminum feeding kit, which includes the following items:    * Non-metallic liner - designed to minimize the amount of friction on the wire    * U-shaped drive rolls - to avoid crushing or deforming the soft aluminum wire. These drive rolls do not shave the wire like V-groove drive rolls. Using V-groove drive rolls, the resulting wire shavings can clog the liner and lead to feeding problems.    * Inlet and outlet guides - designed specifically to avoid wire shaving.    * Contact tips - as compared to those used for the same diameter of steel wire electrode, contact tips for aluminum have larger diameter holes, since as aluminum heats up, it expands more than steel. Therefore, contact tips for aluminum applications are sized small enough to maintain good electrical contact, but large enough to allow for expansion.Load Wire Into the MachineThere is a trick to properly loading aluminum wire into a wire feed welder. While the same technique should be used with steel wire electrodes, it is especially important with aluminum wire loading, to avoid feeding problems during welding.With one hand, hold the wire spool securely so it doesn't unravel. Once you remove the cellophane wrapping, hold the loose end of the wire with the other hand - don't let go until you lock the wire into the drive roll.Inexperienced operators commonly let go of the loose end and the spool starts to unravel. If this happens, it cannot be wound back up and still perform properly - you will have to purchase another spool.Set the Wire Brake TensionThe idea is to have just enough tension to keep the wire from unraveling, but not too much tension so that it causes a drag on the wire. To do this, set the wire spool brake tension for a minimum setting. Then, load the spool on and feed it through the drive rolls. With everything stopped, if the spool keeps turning by itself, there is not enough brake tension. Be careful though, since too much brake tension can put excessive force on the wire.And, operators shouldn't be surprised at the end of the spool if they cannot feed the last few turns; usually the wire is too stiff to come off easily.Set the Drive Roll TensionThis step is probably the most important in the whole set-up process. The experts from Lincoln recommend holding the nozzle about 1" away from an electrically insulated surface at a slight angle. Then, set the drive roll tension close to minimum. Pull the trigger and watch the behavior - as the wire touches the insulated surface, the drive rolls should slip. Tighten down from that point until the wire stops slipping. Again, a word of caution, as wire that is set too tight will tend to 'birdnest'. This means the wire stops at the gun but the drive rolls are still turning. The result is wire feeds out of the drive rolls and birdnests, or backs up and tangles, anywhere along the drive path - at the guide tubes, in the gun liner, etc.Remember, as you set the drive roll tension in the manner described above, that when the gun trigger is pressed, the wire is electrically hot, so always wear a quality pair of welding gloves.Ensure Good Electrical ConnectionsThe work clamp should be securely attached to the welding piece in an area free from paint and contaminants. To clean the piece, use a degreasing solvent to remove any oil and grease. Be sure that the surface is dry before you weld. Also, do not weld with flammable material nearby, such as a container of solvent or paint. As a second step, use a clean, stainless steel wire brush to remove all oxides from the surface of the aluminum.Position Is ImportantAs you are welding, keep the gun cable as straight as possible to minimize feeding restrictions on the soft aluminum wire. A bend in the gun cable can make the wire kink and feed poorly.Practice, Practice, Practice!There is no substitute for practice. Just as a high-quality musical instrument won't make you a good player without practice, a welding operator needs to hone his or her skills as well. Before too long, you and your welder will be making beautiful music (or at least welds) together
Reply:hope yall enjoy
Reply:It is a very nice post but.....You might want the actual authors credit for this.http://www.lincolnelectric.com/knowl...compactmig.asp
Reply:Hmmmmmm  Kinda funny... I've had some good luck on 60xx alloys using a .030" 5356 wire..... (on 1/16 to 1/8" thick mat'l with NO preheat)  using my Northern tools Mig 135.  They must be talking about thier welders
Reply:Hmm I think the best way to weld aluminum sheet in the range that a 115v mig would, is to sell the mig and use the money to buy a torch setup....
Reply:Originally Posted by assassin_workshope yall enjoy
Reply:Originally Posted by weldrwomnIt is a very nice post but.....You might want the actual authors credit for this.http://www.lincolnelectric.com/knowl...compactmig.asp
Reply:Don't worry, you won't get ANY credit whatsoever...Should have saved yourself the trouble, and just posted the link so everyone would know where the information came from off the hop.Foolish EndevorLater,Jason
Reply:Originally Posted by Black WolfDon't worry, you won't get ANY credit whatsoever...Should have saved yourself the trouble, and just posted the link so everyone would know where the information came from off the hop.Foolish Endevor
Reply:I don't respond because of his lack of punctuation. I can't figure out where one thought ends and the next begins. I almost threw my computer out the window it was bothering me so much. I don't even need correct grammer or spelling, but at least give it a try.Thats how I knew he didn't type that long artical long before someone called him out.If you cannot convince them, confuse them.         Harry S Truman
Reply:Originally Posted by 7A749You're just digging yourself in deeper & deeper.The reason you are getting the responses you're getting is entirely due to your attitude.You mentioned that you would listen to some "master certified" welders.You have already heard from several, including the individual you just responded to. A few of them probably have learned more & forgotten more than you will ever know.Kinda like walking into a biker bar & throwing your weight around.If you ain't the real deal, you're gonna get trounced.If you had come here with a different attitude, the way you are being treated now would be much different indeed.IMHO of course
Reply:Originally Posted by 500HpSilveradoI don't respond because of his lack of punctuation. I can't figure out where one thought ends and the next begins. I almost threw my computer out the window it was bothering me so much. I don't even need correct grammer or spelling, but at least give it a try.Thats how I knew he didn't type that long artical long before someone called him out.
Reply:I said it didnt need to be correct, just a try.If you cannot convince them, confuse them.         Harry S Truman
Reply:Sorry you stated "I don't even need correct grammar or spelling, but at least give it a try." which is or be understood as i have bad spelling sorry if i misunderstood on it.
Reply:Originally Posted by 7A749You're just digging yourself in deeper & deeper.The reason you are getting the responses you're getting is entirely due to your attitude.
Reply:not going to read all that years ago when i only had my weld pac 100 my hot water tankleaked in my camper i got the alumkit for it  was $60.00 did the job
Reply:Give it a rest already guys.  Sheesh.MM350P/Python/Q300MM175/Q300DialarcHFHTP MIG200PowCon300SMHypertherm380ThermalArc185Purox oaF350CrewCab4x4LoadNGo utilitybedBobcat250XMT304/Optima/SpoolmaticSuitcase12RC/Q300Suitcase8RC/Q400Passport/Q300Smith op
Reply:for the people on this post that were cool thanks for reading the thread. Yes i do agree that this got way to far. So anyone that i offended i do apologize. For the people that decided to be asses to me yall can go phuck yourself. Remember it was only a thread and it was only to pass some knowledge who cares where it came from or who wrote it. If a priest reads out of the bible does he get the credit for what he says? No, it's all about spreading the good word. So please dont be an *** on a post just read it if you like it great say thanks for the thread and leave all the negativity out.
Reply:Hey, I am all for letting things go....And DR33 is correct - This thread has gone on WAY too long....I will say though, that your sentiment of "Leaving all the negativity out" would come across as being much more sincere, if you hadn't invited everyone to "Initiate Intercourse with Themselves" in the third sentence....In any event, Have a Good Weekend.Last edited by Black Wolf; 05-01-2010 at 02:39 AM.Later,Jason
Reply:Now, dang it, Jason, you're goin' and doin' it on us again---gettin all practical, and all...
Reply:Originally Posted by 7A749Attitude?Where?Oh, here......Yeah, this is SOOOOOO worn out.I'm done
Reply:Originally Posted by TEKNow, dang it, Jason, you're goin' and doin' it on us again---gettin all practical, and all...
Reply:Originally Posted by Black WolfDon't worry, you won't get ANY credit whatsoever...Should have saved yourself the trouble, and just posted the link so everyone would know where the information came from off the hop.Foolish Endevor
Reply:Not using capitalization, poor punctuation and grammar, they all bother me a little but I have never said anything to anyone about it on the internet. Why? Well first off, I make mistakes in those areas too (hypocrite). Second, what am I the internet police? And third maybe they didn't finish high school and they just aren't that smart but it doesn't necessarily make them bad people. Is this Weldingweb.com or Englishweb.com?“Life is not a journey to the grave with intentions of arriving safely in a pretty well-preserved body, but rather to skid in broadside, thoroughly used up, totally worn out and loudly proclaiming ... WOW! What a ride!”
Reply:Originally Posted by Black WolfMy Bad.... LOLHave a Good Weekend.Originally Posted by regularfellaIt's spelled "endeavor" . Here's a link...........http://www.merriam-webster.com/dictionary/endeavor
Reply:I noticed a spelling error in my post above, but I cannot edit the post to correct it.Just thought I would point it out as to not offend anyone.What can I say?  I use a wireless keyboard... Sometimes it doesn't "type" all the letters that I want, and sometimes it doesn't backspace as quickly as I want before I start typing again.. It's my fault for the speed that I type. I don't proof read every word in every post.Last edited by Black Wolf; 05-01-2010 at 05:39 PM.Later,Jason
Reply:Jeez,I can't even post a comment, let along spell correctly.I see this place has not changed.Tim Beeker.
Reply:Dis iz absoflutely rediclufus!  Me thinks it b time ta cloze up dis descustion.MM350P/Python/Q300MM175/Q300DialarcHFHTP MIG200PowCon300SMHypertherm380ThermalArc185Purox oaF350CrewCab4x4LoadNGo utilitybedBobcat250XMT304/Optima/SpoolmaticSuitcase12RC/Q300Suitcase8RC/Q400Passport/Q300Smith op