Day 4 - Tig

admin

Alright, here's my latest progress150 Amp3/32 GREEN Tungsten (changed from red)Balance between 5.5 - 7.0 Attached ImagesAcademyKP03Miller Sychcrowave 200
Reply:How did you like Green or Pure.  Welds are looking better.  JohnSMAW,GMAW,FCAW,GTAW,SAW,PAC/PAW/OFCand Shielding Gases.  There all here. :
Reply:Originally Posted by weldgaultHow did you like Green or Pure.  Welds are looking better.  John
Reply:See how much better they are ....they already look better than my Tig beads weld it like you own it
Reply:Originally Posted by AcademyKP03Thanks! Well, with the pure tungsten; the arc was a bit easier to get because the end of electrode had turned into a little "ball" - which helped.  Also seemed that there wasn't as much penetration - not sure how using pure tungsten would effect that ... just my rather novice observation.
Reply:c'mon waiting for day 7   Keep at it weld it like you own it