I still cant seem to get full penetration with overhead open v. I have been running 3/8's plate with 1/16 land and 3/32 and 1/8 gaps and neither seem to be able to fully pen. I have been carrying the key hole through the entire plate but still cant get material on the back side of the plate. any suggestions? oh and since my teacher hasnt donw this since he was in school 20 years ago his not much help.
Reply:What are your settings? Gas? Wire? volts?...DavidReal world weldin. When I grow up I want to be a tig weldor.
Reply:.035 wire 20# CO2, I would tell you the volts but my machine works on scales instead of voltages.
Reply:Can you run a little more heat?I might have to try this one.DavidReal world weldin. When I grow up I want to be a tig weldor.
Reply:you not gonna get a ton of material on the back. when ever you do open root like that with wire feed. i just to my metal core test 2G 3/32 gap 1/16 land. i got if flush with a keyhole across. but youll stilll have to back grind it 3/16 - 1/4 " back and 1/4" wide u groove and fill to pass an inspection. unless you have a bar then its a different story.6G zirconium 702 GTAW 2" xxheavy6G P.E.D. carbon steel GTAW 2" xxheavy3G titanium Gr. 2 - Gr. 7 GTAW up to 3/4" 3G 316L stainless GTAW up to 1" 3G carbon steel GTAW up to 1" 3G Hastalloy GTAW up to 3/4"1G tantalum GTAW up to .060"
Reply:More Volts/Heat...
Reply:possibly try draging the gun slightly and possibly slower if you need pen like that sorry.6G zirconium 702 GTAW 2" xxheavy6G P.E.D. carbon steel GTAW 2" xxheavy3G titanium Gr. 2 - Gr. 7 GTAW up to 3/4" 3G 316L stainless GTAW up to 1" 3G carbon steel GTAW up to 1" 3G Hastalloy GTAW up to 3/4"1G tantalum GTAW up to .060"
发表于 2021-9-1 00:01:53