Anyone have any advice on doing fluxcore on 6g? I can easily do 6010/7018 but one of the shipyards I want to test for is 6010/flux fill cap. Run stringers or weave? 2-3 bead cap? Anyone have pictures to better explain?
Reply:Weld the b&$(/
Reply:I just finished doing 2g and 5g FCAW on pipe to xray standards. In our case, we ran weaves the whole way out, but not sure this would be appropriate advice for you. Best to check with the supervisor or get your hands on the WPS to know for sure.
Reply:Stringers on 6g if you try to weave you will get cold roll/lap whatever yo want to call it. |
|