hey guys new to forum didnt do alot of searching as time is money....heres my question i am looking to weld a lot of 3/8" x3" aluminum flat stock it is anodized i plan on removing that but it was the right price, i have a syncrowave 200 and 350p was thinking of getting spool gun vs tig welding it all .what do you guys think is suitable ?i dont need cosmetics just functionthey will be support stands for alignments about 16" tall probably hold 1500 lb each and plan on over engineering as is
Reply:If you can get away with mig I would definitely go that route. Tig is great but I don't see it even being close to mig , speed wise |
|