when should I use 1% and when should I use 2%? I'm so confused!!thanks
Reply:Use 2% all the time. I had some 1% and didn't care for it, it seems the tip degrades faster.DavidReal world weldin. When I grow up I want to be a tig weldor.
Reply:Ditto.. ...zap!I am not completely insane..Some parts are missing Professional Driver on a closed course....Do not attempt.Just because I'm a dumbass don't mean that you can be too.So DON'T try any of this **** l do at home.
Reply:A good source for information on various tungsten electrode types.http://www.diamondground.com/index.html
Reply:Originally Posted by zapsterDitto.. ...zap!
Reply:2%seems to last longer."Real power is an arcair hand torch with a piece of 3/4 inch carbon and 1500 amps. You feel like Zeus throwing a lightning bolt."