Critique My Welds

admin

Would anyone like to critique them and give me some feedback. Like to hot or to cold to slow or to fast ect ect. Thanks MikeTo hot maybe?????BackSideFirst attempt at fillet weld any suggestions?Fillet BackSideFillet BottomSide
Reply:ok now..you asked for it!!no.. well the first pics look ok for a beginner..however there are instances that call for total penetration or "burn thru"..thats whats happening on the bottom..to stop that you might want to go down 50 amps and try again..on the fillett weld thats ok too but you may want to try spacing the dips out a little more..and go up 20 amps or so..what are we using for equipment?...zap!I am not completely insane..Some parts are missing Professional Driver on a closed course....Do not attempt.Just because I'm a  dumbass don't mean that you can be too.So DON'T try any of this **** l do at home.
Reply:Originally Posted by zapsterok now..you asked for it!!no.. well the first pics look ok for a beginner..however there are instances that call for total penetration or "burn thru"..thats whats happening on the bottom..to stop that you might want to go down 50 amps and try again..on the fillett weld thats ok too but you may want to try spacing the dips out a little more..and go up 20 amps or so..what are we using for equipment?...zap!
Reply:in some instances you cant get to the rear of something your welding so "total penetration" or "burn thru" is actually put on the print..you know when you get total penetration when you keep feeding filler that seems like way too much for where you are......zap!I am not completely insane..Some parts are missing Professional Driver on a closed course....Do not attempt.Just because I'm a  dumbass don't mean that you can be too.So DON'T try any of this **** l do at home.
Reply:Originally Posted by zapsterin some instances you cant get to the rear of something your welding so "total penetration" or "burn thru" is actually put on the print..you know when you get total penetration when you keep feeding filler that seems like way too much for where you are......zap!