critique my welds!

admin

Every morning when i go into work i lay a couple warm up/practice beads on a couple pieces of scrap,  I brought one of them home the other day, and figured id post a couple pics so you guys could critique them!  so lay it on...whats right/wrong with it?  haha Attached Images
Reply:heres a couple more...fyi...my goal with these welds is to have no bleed through whatsoever...most of what im welding is parts that go on the inside of an oil pan, so having bleed through isnt acceptable for asthetic reasons, and its all TIG Attached Images
Reply:What are your settings? Gas flow, amperage, tungsten size, filler size, etc etc?I won't say I'm the greatest expert, but if I had to critique, I'd say your filler wire is a lil thick for the heat you're running on that thin material.Miller Syncrowave 180SDMillermatic 175
Reply:Originally Posted by KubsWhat are your settings? Gas flow, amperage, tungsten size, filler size, etc etc?I won't say I'm the greatest expert, but if I had to critique, I'd say your filler wire is a lil thick for the heat you're running on that thin material.
Reply:Originally Posted by punkfreeridergas flow is at 15 cfh, i believe, but im not sure, tungsten size is 3/32 thoriated, i set the machine at 135 amps and do the rest with my foothey thanks though!  i appreciate the input
Reply:looks like your torch angle is off, thats why there is more metal deposited on one side of the puddle.  Also seems like your moving really fast.  Turn your heat down and move slower.Have we all gone mad?
Reply:I would have to agree with most of what has been said so far. Smaller filler rod, dipped more often, and fix your electrode/torch angle so the top doesn't get undercut.Not sure I would turn it down, the smaller filler rod will force you to speed up.If that's 11ga plate, then anywhere form 120-130 is what I would usually run.I'd be using 1/16" filler to make it look a little nicer to the eyes.It also looks like your filler rod hand is the unsteady one, make sure you cut the rod in 1/2 before starting to give better control. Make sure you are adding filler as close to parallel to the bead as possible. If you run a few practice beads everyday, stack up the week's worth of trying different settings and hand positions etc, and destructive test them on friday after work.Lets you know what is working on the outside and the inside.
Reply:weld looks good, but i think the end of the weld is a little weak and sloppy looking, should end as good or better than the rest of the weld, but the end looked a little thin
Reply:Originally Posted by revhardIt also looks like your filler rod hand is the unsteady one, make sure you cut the rod in 1/2 before starting to give better control.