okay so i've been practicing a lot of aluminum lately and i tried my first outside corner joint and here it is not perfect but i don't think its to bad. also when doing tee joints i have a hard time finding a good position to weld the fillet joint what do you guys like to do for a weld like that?miller bobcat 250 ntsouth bend metal latheClausing verticle millrikon 17" bandsaweverlast 250exharris oxyfuel set upspeedglass AD helmet with adflo power respirator.
Reply:Dont look bad! The dip is consistent. But looks like your either 1) using a large diameter filler rod. or 2) shoving alot of filler in the puddle. All in all not bad.. Practice Practice What size filler you using? Amps?Owner G&S Mobile Welding & Millwright Services, LLCSpencerville, Ohio Adult Ed. Instructor at Apollo Career Center Lima, Ohio
Reply:amps were 155 on the machine about 3/4 to full on the pedal 1/8 filler rod. probably a bit big since im doing 1/8" aluminummiller bobcat 250 ntsouth bend metal latheClausing verticle millrikon 17" bandsaweverlast 250exharris oxyfuel set upspeedglass AD helmet with adflo power respirator.
Reply:I would, but I can't say anything when it comes to TIG, I'll wait for Zap to inform you about your weld.There are no problems. There are only solutions. It's your duty to determine the right one.Hobart Handler 210Airco 225 Amp MSM Stinger
Reply:Not bad, try using a smaller filler rod.www.thefusionsolution.com |
|