Gas shielded flux core

admin

he company that I work for is cheaper then cheap.  Step over a dollar for a dime every time.  We have been using Washington Alloy 71t-m for our bucket building.  I have burned over 500 lbs of it and like it.  I admit that it is the first wire of this kind that I have used.  Today our supplier brought me techniweld 71t-1, as a comparable wire.  I don't like how it is running.  I was looking for input.  Is this just me?  The beads do not look as good, and seems like it is more likely to melt.  I am wondering weather to send back the TW for WA, or get used to the TW because it is the better wire.  I am running a miller s-32-p feeder off a sa250.Bruce DeLaetHeavy Equipment Mechanic and Welder1948 SA-200 short hood1949 LincWelder 1801963 SA-200 red faceMiller S-32-P