Happy Father's Day to me!

admin

Yay! Stopped by the LWS today. 10 lbs of 6011 to practice with.  Maybe by the time I get to the last pound I'll post some more beads to critique. Also, the supplier told me I should be running AC with 6011, not DCEP. Any truth to this? Attached Images
Reply:what does the package say?Miller thunderbolt 250Decastar 135ERecovering tool-o-holic ESAB OAI have been interested or involved in Electrical, Fire Alarm, Auto, Marine, Welding, Electronics ETC to name a just a few. So YES you can own too many tools.
Reply:It will run on both AC and DCEP.  Sent from my DROID3 using Tapatalk 2Jay DavisAWS-CWIC-60 Specialty Welding ContractorLoving husband, and father of two boys (
Reply:I run 6011 on DC all the timeDisclaimer; "I am just an a$$hole welder, don't take it personally ."
Reply:I have successfully run 6011 on both AC and DCEP........ I prefer 6010 5P+ over 6011........ it looks better....... and you should try 7018 rod...... it's  so much nicer looking..... it's not a whip rod so you just drag it.....Precision TIG 185 and MP 210Bobcat 225NTCutmaster 42O/A tanks.... 2 Argon tanks...... 2 C25 TanksFacebook...... F2 Metal WorksETSY....... https://www.etsy.com/shop/F2MetalWorksF2MetalWorks.com....... http://www.f2metalworks.com/
Reply:Im 15 and i am a good welder although none of you will believe me but I use 6011 for almost all my welding and i use whip or circles. I also run it on dc positive and have tried it on negative too.Quality is our policy.
Reply:I go through a hundred pounds or so of 6011 ayear, all ran on DCEP. I prefer the Lincoln Murex line of it, performs better on rusty corrals than other brands IMO.
Reply:i sometimes switch over to ac cause i like the way it sounds...
Reply:Originally Posted by eagleman193Im 15 and i am a good welder although none of you will believe me but I use 6011 for almost all my welding and i use whip or circles. I also run it on dc positive and have tried it on negative too.
Reply:Well, I'm going to go out and work on my bench a bit more, and maybe I'll run a few beads while I'm out there. Look for a critique this weld part III coming soon.